Título :	Sorption of lead on modified silica obtained from chrysotile: isotherms application Sorção de chumbo numa sílica modificada obtida da crisotila: aplicação de isotermas
Palabras clave :	lead;adsorption;silica;chumbo;adsorção;sílica
Editorial :	Federal University of Piauí
Descripción :	A silica was modified with three alcoxysilanes with different quantities of nitrogen, whose the silica obtained from chrysotile acid leaching. The modified silicas were applied in lead removal from aqueous solution, obtained the following capacities: 1.41, 0.78 e 0.60 mmol g-1 for the materials containing 3, 1 and 2 nitrogen in organic chains, respectively. The isotherms were adjusted using different models, and each material showed affinity to a model. The interactions were favorable and spontaneous from Freundlich model and Gibbs free energy, respectively. Uma sílica foi modificada com três alcoxissilanos com diferentes quantidades de nitrogênio, onde a sílica foi obtida da lixiviação ácida da crisotila (amianto). As sílicas modificadas foram aplicadas na remoção de chumbo de soluções aquosas, obtendo-se as seguintes capacidades: 1,41, 0,78 e 0,60 mmol g-1 para os materiais contendo 3, 1 e 2 átomos de nitrogênios nas cadeias orgânicas, respectivamente. As isotermas foram ajustadas usando diferentes modelos, onde cada material mostrou afinidade a um modelo. As interações foram favoráveis e espontâneas a partir do modelo de Freundlich e da energia livre de Gibbs, respectivamenteSorption of lead on modified silica obtained from chrysotile: isotherms applicationAbstractA silica was modified with three alcoxysilanes with different quantities of nitrogen, whose the silica obtained from chrysotile acid leaching. The modified silicas were applied in lead removal from aqueous solution, obtained the following capacities: 1.41, 0.78 e 0.60 mmol g-1 for the materials containing 3, 1 and 2 nitrogen in organic chains, respectively. The isotherms were adjusted using different models, and each material showed affinity to a model. The interactions were favorable and spontaneous from Freundlich model and Gibbs free energy, respectively.
URI :	http://biblioteca-repositorio.clacso.edu.ar/handle/CLACSO/77467
Otros identificadores :	https://comunicatascientiae.com.br/comunicata/article/view/4 10.14295/cs.v1i1.4
Aparece en las colecciones:	Núcleo de Pesquisa sobre Crianças, Adolescestes e Jovens - Universidade Federal do Piauí - NUPEC/UFPI - Cosecha

Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.